Full video
|
Sample: S6_9
Surface |
: Silan, Biotin 1/100 diluted (0,1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 16-21_17-20_A |
Area |
: 48,1 x 48,1µm (150x150+334+873) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 115 and 116secs at a constant
current of 82mA.
|
|
|
Full video
|
Sample: S6_9
Surface |
: Silan, Biotin 1/100 diluted (0,1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 16-21_17-20_C |
Area |
: 64,2 x 64,2µm (200x200+430+129) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 68 and 69sec. The current
increases from 68 to 69mA.
- Another bead agglutination is ruptured between 72 and
73sec. The current increases from 74 to 76mA (collision?).
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_B_oben |
Area |
: 48,1 x 48,1µm (150x150+447+292) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 66 and 67sec. The current
increases from 8 to 9mA.
- Another bead is ruptured between 70 and 71sec. The current
increases from 12 to 15mA.
- Another bead is ruptured between 73 and 74sec. The current
increases from 14 to 15mA.
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_B_unten |
Area |
: 48,1 x 64,2µm (150x200+461+741) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 87 and 88sec. The current
increases from 24 to 25mA.
- Another bead is ruptured between 158 and 159sec at a constant
current of 87mA.
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_C_oben |
Area |
: 48,1 x 48,1µm (150x150+450+110) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 87 and 89sec. The current increases from 48 to 54mA.
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_C_mitte |
Area |
: 64,2 x 64,2µm (200x200+445+317) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 24 and 26sec. The current increases from 6 to 9mA.
- A bead agglutination is ruptured between 40 and 45sec. The
current increases from 15 to 17mA.
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_C_unten |
Area |
: 64,2 x 64,2µm (200x200+445+508) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 91 and 92sec. The current increases from 57 to 58mA.
- A part of a bead agglutination is ruptured between 96 and 98sec. The current increases from 60 to 62mA.
- A bead is ruptured between 99 and 100sec (the rest of a bead
agglutination). The current increases from 64 to 63mA.
- A part of a bead agglutinationis ruptured between 148 and 150sec. The current increases from 0 to 86mA.
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_D_oben |
Area |
: 48,1 x 56,2µm (150x175+452+28) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 15 and 17sec at a constant current
of 10mA.
- A bead agglutination is ruptured between 25 and 27sec. The current increases from 16 to 18mA.
- A bead is ruptured between 92 and 93sec at a constant current
of 59mA.
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_D_mitte1 |
Area |
: 48,1 x 48,1µm (150x150+464+213) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 109 and 110sec. The current increases from 76 to 77mA.
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_D_mitte2 |
Area |
: 48,1 x 48,1µm (150x150+476+533) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 24 and 25sec. The current increases from 15 to 16mA.
- A bead is ruptured between 25 and 27sec. The current increases from 16 to 18mA.
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_D_unten |
Area |
: 48,1 x 48,1µm (150x150+469+753) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 19 and 20sec. The current increases from 10 to 12mA.
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_E_mitte |
Area |
: 48,1 x 48,1µm (150x150+473+430) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 58 and 60sec. The current increases from 22 to 23mA.
- A bead agglutination is ruptured between 124 and 125sec at a
constant current of 63mA.
|
|
|
Full video
|
Sample: S6_10
Surface |
: Silan, Biotin 1/10 diluted (1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-21_16-20_E_unten |
Area |
: 48,1 x 48,1µm (150x150+478+621) |
- The current given in the video flows through the left wide conducting line.
- A bead is ruptured between 84 and 86sec at a constant current
of 41mA.
|
|
|
Full video
|
Sample: S6_11
Surface |
: Silan, Biotin 1/100 diluted (0,1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-22_18-19_A_oben |
Area |
: 48,1 x 64,2µm (150x200+477+156) |
- The current given in the video flows through the right wide conducting line.
- A bead agglutination is ruptured between 135 and 138sec at a constant current
of 13mA.
- A bead is ruptured between 231 and 232sec. The current
increases from 62 to 66mA.
|
|
|
Full video
|
Sample: S6_11
Surface |
: Silan, Biotin 1/100 diluted (0,1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-22_18-19_A_mitte |
Area |
: 48,1 x 48,1µm (150x150+488+474) |
- The current given in the video flows through the right wide conducting line.
- A bead agglutination is ruptured between 203 and 204sec at a constant current
of 43mA.
- A bead is ruptured between 231 and 232sec The current
increases from 62 to 66mA.
|
|
|
Full video
|
Sample: S6_11
Surface |
: Silan, Biotin 1/100 diluted (0,1µM) |
Beads |
: Micromod (diameter: 1,5µm; Avidin) (1/200: 50µg/ml) |
Video |
: 15-22_18-19_A_unten |
Area |
: 48,1 x 48,1µm (150x150+496+733) |
- The current given in the video flows through the right wide conducting line.
- A bead is slowly ruptured between 127 and 136sec. The current
increases from 7 to 13mA.
|